What are the factors of lattice block in regenerative chamber of glass kiln? ，What does general dredge method have?

What factors are involved in the blockage of the latticework of a glass kiln heat storage chamber? What are the general dredging methods?

① The main factors of heat storage chamber blockage are as follows

a. The inner cavity of the lattice hole inside the heat storage chamber is small, and it is relatively easy to be blocked;

b. The content of ultrafine powder of raw materials is too much, and the water content of compound material is too low, resulting in the dispersion rate of compound material in the kiln is too large;

Oil gun combustion angle is low, so that the flame downward drift blowing material surface, resulting in too much material in the kiln dispersion and with the exhaust gas into the heat storage room:

d, the sulfur content of raw materials and fuel sulfur impurities, so that the exhaust gas has too much sulfide, through the heat storage room in the temperature lattice body parts are easy to cohesion blocked;

② general dredging methods are as follows

a, dredging the heat storage room must be dredged at the right time, but the frequency of dredging is too high not only on the production of a certain impact, but also affect the heat storage room lattice body cycle, so the right time to dredge for the better;

b, with the flame melting removal method dredging (i.e., anti-burning method, so that one side of the heat storage temperature rises by an appropriate amount);

c, with the fire method from the bottom of the heat storage room upward melting lattice hole blocked tuberculosis;

d, from the upper part of the heat storage room downward blowing or upward mechanical dredging:

e. Temporarily open the operation hole to remove the upper layer of blocked knots or the upper layer of collapsed blocked brick.